| Grade: | PA-765A Taiwan Chi Mei |
|---|
| Factory: | Qimei Taiwan |
|---|
| Level: Application | Grade Injection |
|---|
| Brand: | PA-765A Taiwan Chi Mei |
|---|
| Model: | PA-765A |
|---|
CMO authentication data table ABS Taiwan PA-765A
| Items Performance | Condition Test | Method Test | Description Numerical | Company |
| Properties Mechanical | Strength Tensile (lead Zhang Qiangdu) | | ASTM D638/ISO 527 | 400 (5670) | Kg/cm² (MPa) [Lb/in2] |
| Elongation At Break | | ASTM D638/ISO 527 | - | % |
| Modulus Tensile | | ASTM D638/ISO 527 | - | Kg/cm² (MPa) [Lb/in2] |
| Tensile Yield Elongation (elongation) | | ASTM D638/ISO 527 | 20 | % |
| Break Tensile Elongation At (elongation) | | ASTM D638/ISO 527 | - | % |
| Modulus Bending (elasticity bending) | | ASTM D790/ISO 178 | 23000 (32000) | Kg/cm² (MPa) [Lb/in2] |
| Strength Bending | | ASTM D790/ISO 178 | 640 (9070) | Kg/cm² (MPa) [Lb/in2] |
| Hardness Luo's | | ASTM D785 | R-101 | |
| Strength IZOD Notched Impact | 1/4& 23 | ASTM D256/ISO 179 | - | Kg· cm/cm (J/M) ft· lb/in |
| 1/4& -30 | ASTM D256/ISO 179 | 20 (3.7) | Kg· cm/cm (J/M) ft· lb/in |
| 1/8& 23 | ASTM D256/ISO 179 | 24 (4.4) | Kg· cm/cm (J/M) ft· lb/in |
| 1/8& -30 | ASTM D256/ISO 179 | - | Kg· cm/cm (J/M) ft· lb/in |
| Charpy Impact Strength | 23 (GAP) | ASTM D256/ISO 179 | - | Kg· cm/cm (J/M) ft· lb/in |
| -30 (GAP) | ASTM D256/ISO 179 | - | Kg· cm/cm (J/M) ft· lb/in |
| 23 (gap no) | ASTM D256/ISO 179 | - | Kg· cm/cm (J/M) ft· lb/in |
| -30 (gap no) | ASTM D256/ISO 179 | - | Kg· cm/cm (J/M) ft· lb/in |
| Property Physical | Gravity Specific (density) | | ASTM D792/ISO 1183 | 1.17 | |
| Molding Shrinkage Rate | | ASTM D955 | - | % |
| Index Melt (coefficient flow) | 200 /5kg | ASTM D1238/ISO 1133 | 4.6 | G/10min |
| 220 /10kg | ASTM D1238/ISO 1133 | 46 | G/10min |
| Of Water Absorption Rate 23 /24H | | ASTM D570/ISO 62 | - | % |
| Performance Thermal | Heat Distortion Temperature | Annealing | ASTM D648/ISO 75 | 85 (185) | (Fahrenheit degrees) |
| Annealing No | ASTM D648/ISO 75 | 76 (169) | (Fahrenheit degrees) |
| VEKA Softening Point | | D1525/ISO R306 ASTM | 92 (198) | (Fahrenheit degrees) |
| Point Melting | | - | - | (Fahrenheit degrees) |
| Combustion (rate) | | UL94 | 2.1mm, 2.5mm 5VA, V-0 | |
| Linear Expansion Coefficient | | ASTM D696/ISO 11359 | - | Mm/mm. |
| Conditions Processing | Condition Drying | | | Under 80° About 2~3 Hours; C | |
| Temperature Processing | Nozzle | | 180~220° C | C |
| End Front | | 190~220 | C |
| Barrel Material | | 190~220 | C |
| Section Post | | 180~220 | C |
| Temperature Melt | | | - | C |
| Temperature Mould | | | 40~70° C | C |
| Pressure | Pressure Injection | | 50~60kg/cm² | Mpa |
| Pressure Holding | | 40~50kg/cm² | Mpa |
| Pressure Back | | 5~10kg/cm² | Mpa |
| Speed Screw | | | - | RPM |
| Other | Remarks | The hot melt glue in the heating pipe for long time in injection cycle Do Not Heat |
| Color | - |
| Characteristic | High Flame Burning |
| Use | Products spare / parts power tools spare / parts machine etc. Computer / shell TV / Parts Electronic |