PBT 1100 IV 1.0 is a general purpose grade base resin, with non-reinforced, medium viscosity, which can be used in injection molding. |
|||
|
Properties |
Unit |
Standard |
Typical Value |
|
PHYSICAL PROPERTIES |
|||
|
Density |
g/cm3 |
ASTM D792 |
1.31±0.02 |
|
Intrinsic Viscosity |
dl/g |
ASTM D445 |
1.0±0.020 |
|
Melting temperature |
℃ |
ISO 11357, DSC Way |
224.0±2.0 |
|
Melt Flow Rate，235℃/2.16kg |
g/10min |
ASTM D1238 |
20.0-25.0
|
|
Melt Flow Rate，250℃/2.16kg |
g/10min |
ASTM D1238 |
30.0-45.0
|
|
Melt Flow Rate，250℃/5.00kg |
g/10min |
ASTM D1238 |
68.0-78.0 |
|
CEG(Carboxyl End Groups) |
meq/kg |
Potentiometric titration |
≤30 |
|
Color b |
Hunter Lab Photometer |
(D65,10º) |
≤5.0 |
|
Color L |
Hunter Lab Photometer |
(D65,10º) |
≥91.0 |
|
Ash Content |
% |
ASTM D5630-06 |
≤0.035 |
|
Moisture Content |
% |
ASTM D570 |
≤0.30 |
|
Chip Powder Content |
PPM |
GB T9345.1-2008 |
≤50 |
|
Chip Size |
g |
Bluestar Internal Standard |
2.0±0.2 |
|
MACHANICAL PROPERTIES |
|||
|
Tensile Strength（50mm/min） |
MPa |
ASTM D638 |
50-60 |
|
Tensile Elongation |
% |
ASTM D638 |
≥80 |
|
Flexible Strength |
MPa |
ASTM D790 |
≥75 |
|
Izod Impact, notched, 23℃ |
KJ/M2 |
ASTM D256 |
≥4.0 |
|
THERMAL PROPERTIES |
|||
|
HDT, 1.80MPa, 3.2mm |
℃ |
ASTM D648 |
55 |