Manufactured from non-asbestos beater sheet(100% not contain asbestos)with mechanically clinched to 0.18 ~ 0.25mm thick carbon steel tanged (perforated) metal sheet - 08F tinplate insert. It is best gasket material for motorcycle and automobile cylinder head gasket.
This series include:
1) Reinforced non-asbestos Composite Sheet
2) Reinforced non-asbestos Composite Sheet with Both Size Coating Graphite
3) Two or more Layers Steel Inserted Reinforced Non-Asbestos Sheet
4) Reinforced Non-Asbestos Sheet With Both Size Coating Silicon Resin (anti stick)
Available Size: Thickness:1.0mm ~ 3.0mm
400mm x 1000mm ,500mm x 1000mm ,500mm x 1200mm ,500mm x 1500mm
510mm x 1016mm ,510mm x 1530mm ,1000mm x 1000mm ,1000mm x 1500mm
Color: Gray, Black
The other size is optional or according to the requirements of customers.
Product Date Sheet
|
Item |
Standard data |
|
|
Density g/cm³ |
1.3～1.5 |
|
|
working temperature ℃ |
150～300 |
|
|
Compressibility % |
10±5 |
|
|
Recovery ≥ % |
40 |
|
|
Sealing performance |
<0.5cm3/min |
|
|
causticity |
Cusp no rusty |
|
|
Tensile strength MPa ≥ |
12.7 |
|
|
Compressive Strength MPa ≥ |
80.0 |
|
|
Carbon content ≥ % |
98 |
|
|
Ash content ＜% |
1 |
|
|
With the temperature of 150±2℃,Soaking 20# fluid oil for 5 hours, MPa≥ |
oil absorption %≤ |
25 |
|
Thickness-increasing %≤ |
0～10 |
|
|
Stripping performance |
No stripe |
|
|
With the temperature of 15 to 30℃,Soaking 75# kerosene for 5 hours, MPa≥ |
oil absorption %≤ |
15 |
|
Thickness-increasing %≤ |
0～15 |
|
|
Stripping performance |
No stripe |
|
|
With the temperature of 100℃,Soaking distilled water for 5 hours, MPa≥ |
water absorption %≤ |
15 |
|
Thickness-increasing %≤ |
0～15 |
|
|
Stripping performance |
No strip |
|