CMO authentication data table ABS Taiwan PA-765A
| Grade: | PA-765A Taiwan Chi Mei |
|---|---|
| Factory: | Qimei Taiwan |
| Level: Application | Grade Injection |
| Brand: | PA-765A Taiwan Chi Mei |
| Model: | PA-765A |
Items Performance Condition Test Method Test Description Numerical Company Properties Mechanical Strength Tensile (lead Zhang Qiangdu) ASTM D638/ISO 527 400 (5670) Kg/cm² (MPa) [Lb/in2] Elongation At Break ASTM D638/ISO 527 - % Modulus Tensile ASTM D638/ISO 527 - Kg/cm² (MPa) [Lb/in2] Tensile Yield Elongation (elongation) ASTM D638/ISO 527 20 % Break Tensile Elongation At (elongation) ASTM D638/ISO 527 - % Modulus Bending (elasticity bending) ASTM D790/ISO 178 23000 (32000) Kg/cm² (MPa) [Lb/in2] Strength Bending ASTM D790/ISO 178 640 (9070) Kg/cm² (MPa) [Lb/in2] Hardness Luo's ASTM D785 R-101 Strength IZOD Notched Impact 1/4& 23 ASTM D256/ISO 179 - Kg· cm/cm (J/M) ft· lb/in 1/4& -30 ASTM D256/ISO 179 20 (3.7) Kg· cm/cm (J/M) ft· lb/in 1/8& 23 ASTM D256/ISO 179 24 (4.4) Kg· cm/cm (J/M) ft· lb/in 1/8& -30 ASTM D256/ISO 179 - Kg· cm/cm (J/M) ft· lb/in Charpy Impact Strength 23 (GAP) ASTM D256/ISO 179 - Kg· cm/cm (J/M) ft· lb/in -30 (GAP) ASTM D256/ISO 179 - Kg· cm/cm (J/M) ft· lb/in 23 (gap no) ASTM D256/ISO 179 - Kg· cm/cm (J/M) ft· lb/in -30 (gap no) ASTM D256/ISO 179 - Kg· cm/cm (J/M) ft· lb/in Property Physical Gravity Specific (density) ASTM D792/ISO 1183 1.17 Molding Shrinkage Rate ASTM D955 - % Index Melt (coefficient flow) 200 /5kg ASTM D1238/ISO 1133 4.6 G/10min 220 /10kg ASTM D1238/ISO 1133 46 G/10min Of Water Absorption Rate 23 /24H ASTM D570/ISO 62 - % Performance Thermal Heat Distortion Temperature Annealing ASTM D648/ISO 75 85 (185) (Fahrenheit degrees) Annealing No ASTM D648/ISO 75 76 (169) (Fahrenheit degrees) VEKA Softening Point D1525/ISO R306 ASTM 92 (198) (Fahrenheit degrees) Point Melting - - (Fahrenheit degrees) Combustion (rate) UL94 2.1mm, 2.5mm 5VA, V-0 Linear Expansion Coefficient ASTM D696/ISO 11359 - Mm/mm. Conditions Processing Condition Drying Under 80° About 2~3 Hours; C Temperature Processing Nozzle 180~220° C C End Front 190~220 C Barrel Material 190~220 C Section Post 180~220 C Temperature Melt - C Temperature Mould 40~70° C C Pressure Pressure Injection 50~60kg/cm² Mpa Pressure Holding 40~50kg/cm² Mpa Pressure Back 5~10kg/cm² Mpa Speed Screw - RPM Other Remarks The hot melt glue in the heating pipe for long time in injection cycle Do Not Heat Color - Characteristic High Flame Burning Use Products spare / parts power tools spare / parts machine etc. Computer / shell TV / Parts Electronic